Zirconia balls (ZrO2) feature diameters from 0.1mm to 63.5mm, G5-G40 grade, hardness HRC70-73 (HV1100-1300), and density of 6g/cm³. They offer high strength, low wear, chemical stability, and thermal resistance. Widely used in bearings, valves, nozzles, medical, aerospace, and high-wear environments.
Silicon Nitride Balls (Si3N4) are lightweight (1.59% the density of steel), hard (HRC75-80), and offer excellent wear and high-temperature resistance (up to 1050°C). Their smooth surface (Ra 0.01-0.1μm) minimizes friction, making them ideal for high-speed bearings, aerospace, oil drilling, and electronics applications.
Aluminum balls are mainly used in the stud welding industry in place of fasteners for construction, industrial and automotive applications.
Inquire NowZirconia balls (ZrO2) feature diameters from 0.1mm to 63.5mm, G5-G40 grade, hardness HRC70-73 (HV1100-1300), and density of 6g/cm³. They offer high strength, low wear, chemical stability, and thermal resistance. Widely used in bearings, valves, nozzles, medical, aerospace, and high-wear environments.
Inquire NowSilicon Nitride Balls (Si3N4) are lightweight (1.59% the density of steel), hard (HRC75-80), and offer excellent wear and high-temperature resistance (up to 1050°C). Their smooth surface (Ra 0.01-0.1μm) minimizes friction, making them ideal for high-speed bearings, aerospace, oil drilling, and electronics applications.
Inquire NowAluminum balls are mainly used in the stud welding industry in place of fasteners for construction, industrial and automotive applications.